ZF-W170 water-based fluorocarbon coating for outer wall


Color of films: all kinds of colors

Gloss: Website data update...

Packing specification: 20±1kg/barrel

Mixing ratio: 10:1

Actual spreading rate: Metallic Paint 4-6㎡/kg

Film thickness of coating: 30-40μm/track

Dry film of varnish: 10-15μm/track

  • Content
  • Picture Set

Product Introduction:


This product adopts high-quality water-based fluororesin as the base material, mixed with inorganic ceramic pigment and high-performance auxiliaries. It is a kind of super high-quality room-temperature two-component water-based fluorocarbon coating which as super strong weather resistance, high decoration and high self-cleanliness. It is appropriate for the fields of architectural outer wall. The outdoor service life could be more than 20 years


Craft system:


Serial No.

Technological Process

Product used

Technological Requirements

Specific Details

1

Pretreatment of base materials

Level, no obvious hollows and humps

Clean the dirt, grease, mortar residue and so on

2

Water-based permeation seal up primer

ZF-WB270

Permeate in balance, and permeate 1.5-2mm

Roller coat or spray, 18-20/kg, viscosity is 13s

3

Dry

Surface dry

Dry in normal temperature for 3min

4

Anti-crack putty dedicated for outer wall

Putty layer is level and balanced, no cavities and blow holes

Moisture content of wall 8%, PH10, size is used out within 4h

Level putty dedicated for outer wall

Plaster putty dedicated for outer wall

Polishing putty dedicated for outer wall

5

Polish

100-200 abrasive papers

Level, balanced, with certain roughness

After dry, polish until level, clean the dusts

6

Water-based seal primer

ZF-WB180

Film is balanced without holiday

10-20μm, 10/kg, roller coat or brush coat

7

Dry in the air

Surface dry

Still standing for 10-15min, adopt wet-on-wet technique with the next coating

8

Water-based fluorocarbon primer

ZF-WY170

Glossy and balanced, no sagging and flooding

Proportional allocation, viscosity of 50±10s (coating -4 cups)dry firm 15-20μm4-6/kg

9

Dry in the air

Surface dry

Still standing for 10-20min, adopt wet-on-wet technique with the next coating

10

Water-based fluorocarbon finishing coat

ZF-W170

Film is level, color and gloss are balanced

Stir in balance, viscosity of 50±10s(coating -4 cups), dry film 30-40μm4-6/kg

11

Dry

Film is completely dry (hard dry)

2-3d room-temperature solidifying

12

Water-based fluorocarbon coating varnish

ZF-W175

Glossy and balanced, no sagging

Dry film 15-20μm6-8/kg

13

Dry

Film is completely dry (hard dry)

2-3d room-temperature solidifying


Construction characteristics:


The metal texture and color that specifically owned by ZF-W100 series coating product for thermal-insulation and decorative integrated plate improve the decoration effect of architectural surface. The super ultraviolet irradiation resistance and super strong self-cleanliness extend the service life of the architectural surface.


Application area:


It is used in the outer elevation of various kinds of office buildings, residential buildings, stadiums and so on, which include the surface coating of calcium silicate board, cement board, inorganic resin plate, faux marble and so on.

B-808, International Trade Building or Cetra Building, No. 187, No. 308 National Road, Chengyang District, Qingdao

+86-0532-89080157 , +86-135-8921-7101
+86-0532-89080158

CONTACT

Name *

Email *

Verification Code *

Not see?

Message *


站长统计
站长统计