Product Introduction:
This product adopts high-quality water-based fluororesin as the base material, mixed with inorganic ceramic pigment, high-quality auxiliaries to be produced into room-temperature solidified two-component water-based fluorocarbon coating. its performance could rival the solvent type fluorocarbon coating, and it could be used in the temperature of 25℃-150℃ below zero. It is widely used in the field of aluminum products. It could be solidified in normal temperature by itself to meet the requirements of site construction.
Coating process:
Technical parameter:
Product Name |
Water-based fluorocarbon primer |
ZF-W410 Finish
|
ZF-W415 Shaded varnish |
Appearance |
Light-colored dispersion liquid |
Various color dispersions |
Semitransparent dispersions |
Solid content,%
|
≥45 |
≥50 |
≥42 |
Spray viscosity |
50±10s |
50±10s |
30-40s |
Practical Coverage |
4-6㎡/kg dry firm20um |
4-6㎡/kg dry firm30um |
6-8㎡/kg dry firm20um |
coating / curing agent |
8:1 |
8:1 |
8:1 |
surface dry;(Humidity 50%) |
≤30min ,25℃ |
≤30min ,25℃ |
≤30min,25℃ |
Hard work(Humidity 50%) |
≤3d,25℃ |
≤3d ,25℃ or90±10℃, 20±10min |
≤3d,25℃ |
adhesion,level |
≤1 |
≤0 |
≤0 |
hardness |
HB |
≥H |
≥H |
Scrub resistance,order |
1000 |
≥3000 |
≥3000 |
Alkali resistance (5% NaOH) |
≥168h |
≥168h |
≥168h |
Acid resistance(5% HCL) |
≥168h |
≥168h |
≥168h |
耐人工气候老化 |
一 |
≥3000h |
≥3000h |
Craft product system:
Serial No. |
Technological Process |
Products used |
technological requirements |
Specific Details |
1 |
Preprocessing(Polish) |
100-200 abrasive papers |
Clean the dirt, grease, mortar residue and so on |
100-200 abrasive papers / Grinding wheel,Dust removal |
2 |
Water-based fluorocarbon primer |
ZF-WY410 |
Glossy and balanced, no sagging and flooding |
Proportional allocation, viscosity of 50±10s (coating -4 cups),dry firm 15-20μm,4-6㎡/kg Mixed used out within 4h |
3 |
Surface dry |
|
adopt wet-on-wet technique Process,primer Surface dry |
Still standing for 10-20min or60℃ 10min,humidity≤60% |
4 |
Water-based fluorocarbon finishing coat |
ZF-W410 |
Glossy and balanced, no sagging and flooding |
Thin spray multichannel,viscosity of 50±10s (coating -4 cups), dry firm 30±5μm,4-6㎡/kg,Mixed used out within 4h |
5 |
Dry |
|
room-temperature solidifying 3d or 90±10℃,30±10min |
Film needs to be completely dry |
6 |
Water-based fluorocarbon coating varnish |
ZF-W415 |
Dry film 20±5μm |
1-2order Spray, 6-8㎡/kg |
7 |
Dry |
|
room-temperature solidifying≥3d or90±10℃,30±10min |
Film needs to be completely dry |